PE Cable End caps Heatshrink adhesive lined end caps For Cable Accessories
Product Description
Heatshrink
adhesive lined end caps are used to seal the ends of plastic, rubber
and paper insulated cables, from moisture, dirt and corrosion.
Product Features
Resistant to common fluids and chemicals
Seals and protects cable ends (Waterproof)
Heat Shrink End Caps
Material: Polyolefin
Wall Type: Heavy Wall
Temperature Range: -45~105 C
Shrink Ration: 2: 1
Color: Black
Length:22~270mm
Wire Range: 6~240mm
Shrink Temperature: 110~130 C
Features
The End Cap is adhesive lined to bond with the heat shrink it overlaps;
Hot melt adhesive seals and insulates in one step to speed installation;
Adhesive lining will prevent moisture penetration, allowing for long term storage of cable;
Forms pressure-tight seal on ends of communication and power cables;
Shrink ratio of 2:1 insulates a wide range of diameters and irregular shapes;
Cross-linked UV resistant material improves chemical and temperature resistance;
Continuous use temperature of up to 105°C;
Shrink temperature of 110-130 °C;
Dual wall end cap, with internal wall of hot-melt adhesive provides excellent bonding to plastic and metals;
Capable of sealing the entire surface of a cable or wire.
Technical data
Property | Test Method | Standard Value |
Operating temperature | IEC 216 | -45oC to+105oC |
Tensile strength | ASTM-D 2671 | ≥13MPa |
Elongation at break | ASTM-D 2671 | ≥300% |
Tensile strength after aging | ASTM-D-2671/120oC,168hrs | ≥10MPa |
Elongation at break after aging | ASTM-D-2671/120oC,168hrs | ≥240% |
Dielectric strength | IEC 243 | ≥15kV/mm |
Volume resistance | ASTM-D-2303 | ≥1×1013?.cm |
Dielectric constant | IEC 250 | 3.0 |
Radial shrinkage | - | ≥50% |
Eccentricity | ASTM-D-2671 | ≤35% |
Low Temperature Flexibility | ASTM-D-2671 | -40oC, 4hrs, no cracking |
Minimum shrink temperature | - | 90oC |
Minimum fully recovered temperature |
- | 130oC |
Dimension
Size |
Size after recovery(mm) |
Size as supplied (mm) |
Cable sizes(mm) |
|||
Size |
Inner Diameter |
Wall thickness |
Inner Diameter |
Wall thickness |
length |
Outer Diameter |
Φ 11 |
≤6.5 |
1.1±0.1 |
≥11 |
0.7±0.2 |
≥22 |
Φ6-9 |
Φ 16 |
≤8.0 |
2.5±0.1 |
≥16 |
1.2±0.2 |
≥70 |
Φ9-14 |
Φ 20 |
≤8.0 |
2.5±0.1 |
≥20 |
1.2±0.2 |
≥70 |
Φ9-17 |
Φ 25 |
≤11 |
2.5±0.1 |
≥25 |
1.2±0.2 |
≥80 |
Φ12-22 |
Φ 32 |
≤17 |
2.6±0.1 |
≥32 |
1.5±0.2 |
≥90 |
Φ17-27 |
Φ 40 |
≤15 |
2.8±0.1 |
≥40 |
1.5±0.2 |
≥90 |
Φ20-35 |
Φ 55 |
≤25 |
2.8±0.1 |
≥55 |
1.5±0.2 |
≥125 |
Φ28-45 |
Φ 75 |
≤30 |
3.2±0.1 |
≥75 |
1.8±0.2 |
≥145 |
Φ40-65 |
Φ 100 |
≤42 |
3.5±0.1 |
≥100 |
1.8±0.2 |
≥140 |
Φ50-90 |
Φ 120 |
≤59 |
3.5±0.1 |
≥120 |
1.8±0.2 |
≥155 |
Φ70-110 |
Φ 140 |
≤63 |
4.0±0.1 |
≥140 |
2.0±0.2 |
≥180 |
Φ90-130 |
Φ 250 |
≤94 |
4.0±0.1 |
≥250 |
2.0±0.2 |
≥270 |
Φ120-240 |
PE Cable End caps Heatshrink adhesive lined end caps For Cable Accessories